PRODUCT DATA SHEET
JL1172 / GL1172
POLYURETHANE ADHESIVE
TWO-COMPONENT, SOLVENT-BASED
DESCRIPTION
●Specially designed for lamination of MULTI LAYER PLASTIC FILMS, AL/PLASTIC, VMPET film, like Mask packaging.
●Applicable to dry lamination at various speeds.
●Not suitable for laminating PE film with higher additive content.
PHYSICAL PROPERTIES | ||
Type | JL1172(Main agent) | GL1172(Curing agent) |
Composition | -OH | -NCO |
Appearance | light yellow viscous liquid | light yellow viscous liquid |
Solid content (%) | 72±2 | 70±2 |
Viscosity at 25 °C(mPa.s) | 4500±2000 | 2000±1000 |
Solvent | Ethyl acetate | Ethyl acetate |
Mixing ratio (quality) | 1 | 1 |
Shelf life at 15 ~ 25°C(Months) | 12 | 12 |
CURING
| Curing temperature(℃) | 50±5 |
Curing time(hrs) | 24-48hrs (At least 24hrs of curing for the pre-laminated films is required before the completion of rewinding or laminating of the 3 layer composite film. And It is needed to process the pouch making after the completion of curing perfectly.) |
INSTRUCTIONS
●It may experience interactions with the ink of the pre-laminated composite material, the film additive or the substance of coating layers or the stuff of packing. (esp. below-mentioned substances in higher content: e.g. vinyl acetate in polyethylene film, slip agent, antistatic agent, antimist additive, pigment, etc. ) Therefore it is necessary to examine the interaction of adhesive solution and the composite materials before mass production.
●It is necessary to increase the dosage of curing agent when laminating the polyurethane ink printed materials with no hardener is performed. A test referred to the properties being able to reach the requirement of the quality must be made before mass production.
PACKAGING
| JL1172 Main agent | 20 kg/Bucket |
| GL1172 Curing agent | 20 kg/Bucket |